VOLUME 66 (6/2023)
| TITLE | | NANOHARDNESS AND MODULE OF ELASTICITY OF CR-BASED NITRIDE COATINGS DEPOSITED AT TEMPERATURES BELOW 200C |
| | AUTHOR(S) | | V. Chitanov, E. Zlatareva, L. Kolaklieva, R. Kakanakov, T. Cholakova, S. Kolchev, C. Pashinski |
| | ABSTRACT | | Sets of Cr-based hard coatings were prepared via reactive closed field unbalanced magnetron sputtering (CFUBMS). Substrate temperature was kept in range of 150 to 200ºC during deposition. Nanohardness (H) and effective modulus of elasticity (E*) of the CrN, CrAlN, CrTiN and CrTiAlN coatings were examined using depth-sensing indentation method. The results from the combined examination of the research ratios showed that the triple and quaternary hard coatings have superior mechanical properties and they strongly depend on the deposition conditions. |
| | DOI | | doi.org/10.62853/HXOV5505 |
| | PAGES | | 43-45 |
| | DOWNLOAD | | NANOHARDNESS AND MODULE OF ELASTICITY OF CR-BASED NITRIDE COATINGS DEPOSITED AT TEMPERATURES BELOW 200C |
| | How to cite this article: | | Chitanov V., Zlatareva E., Kolaklieva L., Kakanakov R., Cholakova T., Kolchev S., Pashinski C. Nanohardness and module of elasticity of Cr-based nitride coatings deposited at temperatures below 200ºC. Journal of the Technical University of Gabrovo 66 (2023) 43-45 |
|
|